AISI 1060
Steels containing carbon as the main alloying element are called carbon steels. They contain up to 0.4% silicon and 1.2% manganese. Residual elements such as copper, molybdenum, aluminium, chromium and nickel may also be present in these steels. AISI 1060 carbon steel has characteristics similar to that of AISI 1055 carbon steel.
| Element | Content(%) |
|---|---|
| Iron, Fe | 98.35-98.85 |
| Manganese, Mn | 0.60-0.90 |
| Carbon, C | 0.55-0.660 |
| Sulfur, S | ≤ 0.050 |
| Phosphorous, P | ≤ 0.040 |
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength, ultimate | 620 MPa | 89900 psi |
| Tensile strength, yield | 485 MPa | 70300 psi |
| Modulus of elasticity | 190-210 GPa | 29700-30458 ksi |
| Bulk modulus (typical for steel) | 140 GPa | 20300 ksi |
| Shear modulus (typical for steel) | 80 GPa | 11600 ksi |
| Poissons ratio | 0.27-0.30 | 0.27-0.30 |
| Elongation at break (in 50 mm) | 10% | 10% |
| Reduction of area | 45% | 45% |
| Hardness, Brinell | 183 | 183 |
| Hardness, Knoop (converted from Brinell hardness) | 204 | 204 |
| Hardness, Rockwell B (converted from Brinell hardness) | 89 | 89 |
| Hardness, Vickers (converted from Brinell hardness) | 192 | 192 |
Sheets / Plates
| Production Route | Hot Rolled, Cold Rolled |
| Material Standard | AISI, ASTM, ASME, DIN, BS, EN, ISO, JIS, GOST, SAE, IS & Custom Chemistry |
| Size | Width from 100mm to 3000mm ; Length from 500mm to 12000mm |
| Thickness | 0.1mm to 400mm |
| Delivery Condition | As Rolled, Annealed, Quenched and Tempered, Normalized |
| Surface Finish | Plain, Brushed, Cladded |