| Element | Content(%) |
|---|---|
| Iron, Fe | 98.47-98.94 |
| Manganese, Mn | 0.70-1 |
| Carbon, C | 0.360-0.440 |
| Phosphorous, P | ≤ 0.040 |
| Sulfur, S | ≤ 0.050 |
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength, ultimate | 605 MPa | 87700 psi |
| Tensile strength, yield | 510 MPa | 74000 psi |
| Modulus of elasticity | 190-210 GPa | 29700-30458 ksi |
| Bulk modulus (typical for steel) | 140 GPa | 20300 ksi |
| Shear modulus (typical for steel) | 80 GPa | 11600 ksi |
| Poissons ratio | 0.27-0.30 | 0.27-0.30 |
| Elongation at break | 12% | 12% |
| Reduction of area | 35% | 35% |
| Hardness, Brinell | 179 | 179 |
| Hardness, Knoop (converted from Brinell Hardness) | 204 | 204 |
| Hardness, Vickers (converted from Brinell Hardness) | 187 | 187 |
Sheets / Plates
| Production Route | Hot Rolled, Cold Rolled |
| Material Standard | AISI, ASTM, ASME, DIN, BS, EN, ISO, JIS, GOST, SAE, IS & Custom Chemistry |
| Size | Width from 100mm to 3000mm ; Length from 500mm to 12000mm |
| Thickness | 0.1mm to 400mm |
| Delivery Condition | As Rolled, Annealed, Quenched and Tempered, Normalized |
| Surface Finish | Plain, Brushed, Cladded |