Carbon steels have carbon as the key alloying element in their composition. They also contain up to 0.4% silicon and 1.2% manganese. In addition, the residual elements such as copper, molybdenum, aluminium, chromium and nickel are present in these steels. AISI 1035 is a water resisting carbon steel whose wear resistance and hardenability are increased by the addition of small quantity of chromium.
Element | Content(%) |
---|---|
Iron, Fe | 98.63-99.09 |
Manganese, Mn | 0.60-0.90 |
Carbon, C | 0.310-0.380 |
Sulfur, S | ≤ 0.050 |
Phosphorous, P | ≤ 0.040 |
Properties | Metric | Imperial |
---|---|---|
Tensile strength, ultimate | 585 MPa | 84800 psi |
Tensile strength, yield | 370 MPa | 53700 psi |
Modulus of elasticity | 190-210 GPa | 29700-30458 ksi |
Bulk modulus (typical for steel) | 140 GPa | 20300 ksi |
Shear modulus (typical for steel) | 80 GPa | 11600 ksi |
Poissons ratio | 0.27-0.30 | 0.27-0.30 |
Elongation at break (in 50 mm) | 30% | 30% |
Reduction of area | 53% | 53% |
Hardness, Brinell | 183 | 183 |
Hardness, Knoop (converted from Brinell hardness) | 204 | 204 |
Hardness, Rockwell B (converted from Brinell hardness) | 89 | 89 |
Hardness, Vickers (converted from Brinell hardness) | 192 | 192 |
Machinability (based on AISI 1212 steel. as 100 machinability) | 65 | 65 |
Production Route | Hot Rolled, Cold Rolled |
Material Standard | AISI, ASTM, ASME, DIN, BS, EN, ISO, JIS, GOST, SAE, IS & Custom Chemistry |
Size | Width from 100mm to 3000mm ; Length from 500mm to 12000mm |
Thickness | 0.1mm to 400mm |
Delivery Condition | As Rolled, Annealed, Quenched and Tempered, Normalized |
Surface Finish | Plain, Brushed, Cladded |